Carbon
Science
Vol. 3, No. 3 September 2002 pp. 142-145
Development of Carbon Nanotubes and Polymer Composites Therefrom
P. K. Jain*
ª
, Y. R. Mahajan*, G. Sundararajan*, A. V. Okotrub**,
N. F. Yudanov** and A. I. Romanenko**
*International Advanced Research Center for Powder Metallurgy and New Materials, Hyderabad-500 005, India
**Institute of Inorganic Chemistry, SB RAS, Pr. Lavrent’eva 3, Novosibirsk 630090, Russia
ª
e-mail:
*arcint@hdl.vsnl.net.in *spectrum@che.nsk.su
(Received July 10, 2002; accepted September 4, 2002)
Abstract
Multiwall carbon nanotubes (MWNT) were produced using the arc-discharge graphite evaporation technique. Composite
films were developed using MWNT dispersed in polystirol polymer. In the present work, various properties of the polymeric
thin film containing carbon nanotubes were investigated by optical absorption, electrical resistivity and the same have been
discussed.
Keywords :
carbon nanotube, arc-discharge evaporation, polymer composite
1. Introduction
1 cm. The d.c. arc current was typically 800 Ampere at 35-
40 Volts. The arc vaporisation was carried out in He gas of
The discovery of the carbon nanotubes has created enor-
mous interest in the recent years due to their unique
structures and properties [1]. This led to much speculation
about their unexplored properties and potential applications
[1-3]. It has been established that depending upon the
structure, they are either metallic or semiconducting and
also have exceptional mechanical properties [4-5]. However,
the actual applications of the carbon nanotubes are still to be
explored in commercial terms. Since the size of the particles
are in the in order of nano-dimesnsions, new technology
become apparent but control and manipulation become diffi-
cult. An attempt has been made to develop the carbon
nanotubes composite films with polymer (Polystrol) and
evaluates its various properties like electrical resistivity,
optical properties etc..
2. Experimental
2.1. Development of multiwall Carbon Nanotubes
Multiwall carbon nanotubes (MWNT) were produced
using the arc-discharge graphite evaporation technique
.
The
apparatus for arc discharge graphite evaporation is described
in the Figure 1 [6, 7]. A vacuum chamber of 50 cm in diam-
eter and 150 litres in volume has double water-cooled walls.
The electrodes were installed vertically in the centre of the
chamber. Diameter of the lower graphite cathode was 60
mm. The upper movable anode was combined of seven 6
mm-diameter and 200 mm-length graphite rods (Spectro-
scopic Grade), which were spaced from each other by about
Fig. 1.
Experimental Set Up for the Synthesis of Multiwall Car-
bon Nanotubes 1) Graphite Electrodes, 2) Electric Arc, 3) Water
cooled manipulators, 4) Flexible current leads, 5) Vacuum -tight
current leads, 6) Manipulator drive, 7) Cloth filter, 8) Water
cooled chamber shell, 9) Windows, 10, 11) Finely tuned gas
valves, 12) Movable thermocouple, 13) Vacuum valves and 14)
Pressure setting valves.
Development of Carbon Nanotubes and Polymer Composites Therefrom
143
800 Torr. Simultaneous evaporation of seven rods during 15-
20 minutes produces a carbon deposit at cathode up to 40
mm in diameter and about 30 mm height. The cathode
deposit weight may achieve up to 50 wt% of the evaporated
rods depending on their moving rate and the He gas pres-
sure.
2.2. Development of the composite films
Composite films from Multiwall carbon nanotubes
(MWCNT) dispersed in Polystrol polymer is developed. The
ratio of the MWCNT and the polymer was kept about 50%
by weight and the thickness of the film was around 150-200
microns. Electrical resistivity of the composite films were
measured from 4 K to 300 K by four point contact method.
Optical absorption of the composite film was measured on
Photometer KFK-3 Russian Model in the wavelength range
of 300-1000 nm. Transmission Electron micro-graphs were
taken on JEM-2010.
3. Results and Discussions
Electrode (cathode) deposits of graphite which is mainly
carbon nanotubes (about 70-80%) rest is polyhedral graphitic
phase. The arc discharge process is characterised by ex-
tremely high temperature, presence of electromagnetic fields,
significant pressure and temperature gradients. These ex-
treme conditions make it possible to produce metastable
nanometer-scale carbon structures. Carbon soot condensed
on the water-cooled reactor walls contains cage molecules -
fullerenes C
60
, C
70
, or, when catalytic metal particles are co-
evaporated, single-wall nanotubes (SWCNT) can be pro-
duced. A carbon deposit filled by multiwall nanotubes, poly-
hedral and quasi-spherical particles, and amorphous carbon
growths onto the cathode. The cathode deposit growth rate,
its size and morphology depend on several conditions: type
and pressure of buffer gas; arc current characteristics; size,
configuration and moving rate of electrodes, and the addition
of another elements to the anode material. Usually, the
deposit is defined roughly in two regions, namely, outer 3-5
mm thick part looking as petal-like material from graphite
sheets and inner part consisting of nanoparticles. Figure 2a
shows the scanning electron photograph of the inner part of
the deposit of the pristine material of the carbon nanotubes
that is as deposited on the cathode. Figure clearly shows that
many tubular structures are present along with other graphi-
teic phase. Figure 2b shows the Transmission Electron
Micrographs of the carbon nanotubes. Micrographs clearly
shows that deposit electrode is enrich in the carbon nano-
tubes. However, other graphitic phase is also present which
clearly brings out that separation or purification of the car-
bon nanotube without damaging the end caps is quite dif-
fcult. From the TEM photograph it has been observed that
most of the carbon nanotubes are with closed endings.
Fig. 2.
Micrographs of the Carbon Nanotubes. (a) Scanning
Electron Micrograph (SEM), (b) Transmission Electron Micro-
graph (TEM).
Optical absorption spectra of composite film presented on
Figure 3. In the figure, the curves are shown for only
Polystrol resin film and of the polymeric composite film
containing the carbon nanotubes. From the figure it is clear
that the curve of composites film has about five to six times
less absorption which may be attributed due the presence of
the carbon nanotubes, which are showing absorption. When
these two curves are normalised that is from the curve of
polystrol resin curve of composite film is divided so that the
contribution of the carbon nanotubes alone can be obtained
and the same is plotted in the Figure 3(b). From this curve
there are some additional peaks have observed at about 500
nm, which may be attributed due to the interactions of the
polymer resin and the carbonaceous materials.
Electrical resistivity of the composites films was measured
using four point contact technique in the temperature interval
of 4.2-300 K. The dependence of electrical conductivity with
temperature is shown in Figure 4. Typical behaviour of the
temperature dependence of the conductivity is presented for
the composite film (Figure 4a). In the figure, curve ‘a’ and
‘b’ are of the polymer composite films and curve ‘c’ is of the
144
P. K. Jain et al. / Carbon Science Vol. 3, No. 3 (2002) 142-145
Fig. 3.
Optical Spectra of Polymer and Composite Film. (a)
Polymer and Composite Film, (b) Only Carbon Nanotubes.
Fig. 4.
Electrical Resistivity of the Composites Film (a) and (b)
Polymer Composite Film (c) Pristine Material (Carbon nano-
tubes as deposited). [In Graph ‘a’ values of Curve c is multiply
by 5000 and in Graph ‘b’ curve c is divided by 5000 to make in
same scale’.
as deposited cathode material (Pristine material). Figure 4 is
having linear curve as well as the logarithim scale curve of
the conductivities of the films. Since the resitivity of the
polymer composite film is enormously high as compared to
the pristine material, the curve of the pristine material (curve
c) is normalised to the same scale by dividing it by a factor
of 5000 The temperature dependencies are non-metallic
from 300 K up to 4.2 K, in accordance to the measurements
made for individual multiwall nanotubes and for multiwall
nanotube bundles [8]. Curves in Figure 4 show the following
to the logarithmic temperature dependence. Similar conduc-
tivity dependence, being characteristic of disordered two-
dimensional systems. Such proportion has been shown to be
typical for the two-dimensional disordered conductors. Non-
metallic behavior of
nanotubes [9]. From the electrical resitivity test measured
from 4 K to 300 K, it is evident that the resistivity of the
polymer film is high as compared to the pristine material
(Carbon nanotubes). However it is possible to develop con-
ducting polymer film containing carbon nanotubes.
4. Conclusions
(
T
) may be caused by structural
defects in nanotubes composing the carbonaceous sample.
Actually, the measurements on the individual multiwall nan-
otube demonstrated that the resistivity of defective nano-
tubes is an order of magnitude larger that of straight
s
Developed the Multiwall Carbon Nanotubes (MWCNT)
using the arc-discharge graphite evaporation technique.
Developed the polymeric films containing carbon nanotubes.
It is found that from the optical absorption of the composite
film that the some of the carbon nanotubes have shown the
absorption capabilities. Even though the electrical conductiv-
ity of the polymeric composite film is far less as compared
to the pristine material but conducting polymer films can be
developed by dispersing carbon nanotubes which may find
some good applications in near future.
Development of Carbon Nanotubes and Polymer Composites Therefrom
145
Acknowldgement
270
, 1179
[3] Tans, S. J.; Devoret, M. H.; Dai, M.; Thess, A.; Smalley, R.
E.; Geerligs, L. J.; Dekker, C.
Nature
1997
,
386
, 474.
[4] Mintmire, J. W.; Robertson, D. H.; White, C. T.
J. Phys.
Chem. Solids
.
1993
,
54
, 1835.
[5] Chico, L.; Benedict, L. X.; Louie, L. G.; Cohen, M. L.
Phys. Rev.
1996
,
B54
, 2600.
[6] Okotrub, A. V.; Shevtsov, Yu. V.; Nasonova, L. I.; Sinya-
kov, D. E.; Novoseltsev, O. A.; Trubin, S. V.; Kravchenko,
V. S.; Mazalov, L. N.
Pribory and Tekhnika Experim.
1995
,
1
, 193.
[7] Okotrub, A. V.; Shevtsov, Yu. V.; Nasonova, L. I.; Sinya-
kov, D. I.; Chuvilin, A. L.; Gutakovskii, A. K.; Mazalov, L.
N.
Neorgan. Mater.
1996
,
32
, 974.
[8] Kaiser, A. B.; Dusberg, G.; Roth, S.
Phys. Rev.
1998
,
B 57
,
1418.
[9] Dai, H.; Wong, E. W.; Lieber, C. M.
Science
1996
,
272
,
523.
Authors are thankful to Dr. A.L. Chuvilin from Institute of
Catalyst, Novosibirsk,for helping in the Transmission Elec-
tron Microscopy. We are also thankful to Ms. Chaoying
WANG, from Institute of Physics, Beijing, China for the
Scanning Electron Microscopy This work was supported by
the Russian scientific and technical program «Actual direc-
tions in physics of condensed states» on the «Fullerenes and
atomic clusters» (Projects No 98055) and the Russian Foun-
dation for Basic Research (Projects Nos. 00-02-17987, 00-
03-32510). P K Jain is thankful to Department of Science
and Technology (DST), India for “BOYSCAST” Fellowship.
References
[1] Iijima, S.
Nature
1991
,
354
, 56.
[2] Heer, W. A. de.; Chatelain, A.; Ugarte, D.
Science
1995
,